STOODY 110, 110-G, 110-O, 110-MC

Stoody 110 is a modified chromium, high‑manganese steel filler metal designed for rebuilding manganese steel parts that experience severe impact loading. It provides good toughness and wear resistance, making it suitable as a final hard‑facing layer in extreme impact situations.

Key Features

• Modified chromium, high‑manganese composition
• Excellent toughness and wear resistance
• Ideal for final hard‑facing in high‑impact applications
• Part of ESAB’s extensive Stoody hard‑facing family

Specifications

• Yield Strength: 76 MPa
• Tensile Strength: 119 MPa
• Elongation: 40 %
• Hardness (As Deposited): 17 HRC
• Hardness (Work Hardened): 55 HRC
• Deposition Data:
  • 1.6 mm: 150‑210 A, 22‑26 V, Full Range, TTW 13‑25 mm
  • 2.0 mm: 225‑275 A, 24‑26 V, Full Range, TTW 19‑32 mm
  • 2.4 mm: 225‑300 A, 23‑27 V, Full Range, TTW 25‑38 mm
  • 2.8 mm: 225‑375 A, 23‑27 V, Full Range, TTW 25‑38 mm

Applications

• Hard‑facing of manganese steel parts
• Repair and maintenance of high‑impact components
• Final wear‑resistant layer in severe service conditions